3M™ Dyneon™Fluoroplastic PFA 6505TZ
Perfluoroalkoxy
3M Advanced Materials Division
产品说明：
3M™ Dyneon™ Fluoroplastic PFA 6505TZ (a fully fluorinatedcopolymer of tetrafluoroethylene and perfluorovinylether) hasexceptional temperature resistance, excellent electrical propertiesand excellent chemical inertness and weather resistance. It is usedin molded valves, pumps, tanks, filters and pipes, in heat tracecables and in wire for appliances.
Features
Wide service temperature range
Excellent, almost universal resistance to solvents andchemicals
Extremely high weathering resistance and UV stability
Excellent electrical insulation properties
High limiting oxygen index: Does not support combustion
Smooth surfaces
Good non-stick characteristics
Good low-friction properties
Broad processing window
Improved mold release property
物性信息：
| 基本信息 | |
|---|---|
| 特性 |
|
| 用途 |
|
| 形式 |
|
| 加工方法 |
|
| 物理性能 | 额定值 | 单位制 | 测试方法 |
|---|---|---|---|
| 密度 | 2.15 | g/cm³ | ISO 12086 |
| 熔流率（熔体流动速率） (372°C/5.0 kg) | 5.0 | g/10 min | ISO 1133 |
| 硬度 | 额定值 | 单位制 | 测试方法 |
|---|---|---|---|
| 肖氏硬度 (邵氏 D) | 60 | ASTM D2240, ISO 868 |
| 机械性能 | 额定值 | 单位制 | 测试方法 |
|---|---|---|---|
| 拉伸应力 (断裂, 23°C) | 30.0 | MPa | ISO 527-1 |
| 拉伸应变 (断裂, 23°C) | 410 | % | ISO 527-1 |
| 弯曲模量 | 550 | MPa | ASTM D790 |
| 热性能 | 额定值 | 单位制 | 测试方法 |
|---|---|---|---|
| 熔融温度 | 310 | °C | ISO 12086 |
| 可燃性 | 额定值 | 单位制 | 测试方法 |
|---|---|---|---|
| 极限氧指数 | > 95 | % | ASTM D2863 |
| 注射 | 额定值 | 单位制 | |
|---|---|---|---|
| 加工（熔体）温度 | 250 到 400 | °C |
| 挤出 | 额定值 | 单位制 | |
|---|---|---|---|
| 熔体温度 | < 400 | °C |