PC塑料的粘接
根据不同需要,可以选择以下粘合剂:
1.G-933:单组分常温固化软弹性防震粘合剂,耐高低温,不同粘度粘接速度几秒至几个小时固化完毕。
2.KD-833瞬间粘接剂,可以数秒钟或数十秒钟*粘合PC塑料,但胶层硬脆,不耐60度以上热水浸泡。
3.QN-505,双组分胶,胶层柔软,适合PC塑料大面积粘接或复合。但耐高温性能较差。
4.QN-906:双组分胶,耐高温。
5.G-988:单组份室温硫化胶,固化后是弹性体具有良好的防水,防震粘合剂,耐高低温, 1-2mm厚度的话,10分钟左右初固,5-6小时基本固化,有一定的强度。固化的话需要至少24小时。单组份,不需要混合,挤出后涂抹静置即可,*加温。
6.KD-5606:UV紫外线固化胶,粘合透明PS片材及板材,可达无痕迹效果,需要用紫外线灯照射固化。粘后效果美观。但耐高温性能较差。
Features: 1, high impactstrength, wide range of temperature. 2. High transparency and freedyeing. Three. D. T. High. 4. Excellent electrical characteristics.5, odourless odourless harmless to human health in line with healthand safety. 6. Low forming shrinkage and good dimensionalstability. Electronic and electrical appliances: CD, Switch,appliance case, signal tube, telephone. Industrial parts: CameraBody, machine housing, helmet, diving mirror, safety lens. Mainproperties: A, mechanical properties: high strength, fatigueresistance, dimensional stability, creep is small (high temperatureconditions also * little change) ; B, heat aging resistance: the ULTemperature Index reached 120 ~ 140 ° C (outdoor long-term agingwas also very good) C, Solvent Resistance: no stress cracking; D,to the water stability: under the high temperature meets the waterto be easy to decompose (under the high temperature and highhumidity environment use needs to be careful) ; E, electricalperformance: 1, insulation performance: excellent (wet, hightemperature can also maintain electrical performance stability, isthe manufacture of electronic and electrical parts of the idealmaterial)2, dielectric coefficient: 3.0-3.2; 3, Arc Resistance:120s; F, molding processability: ordinary equipment injection orextrusion. PC plasticadhesive according to different needs, you can choose the followingadhesives: 1. G -933: one-component room-temperature cured softelastic anti-shock adhesive, high and low temperature resistance,different viscosity bonding speed several seconds to several hoursafter curing. 2. KD-833 instant adhesive, can be a few seconds ortens of seconds * PC adhesive plastic, but the adhesive layer ishard and brittle, not resistant to 60 degrees above hot waterimmersion. 3. QN-505, two-component adhesive, soft adhesive layer,suitable for large area of PC plastic bonding or composite. But thehigh temperature resistance is poor. Four. QN-906: two-componentadhesive, high temperature resistance. 5. G-988: one-component roomtemperature vulcanizate, cured elastomer with good waterproof,shockproof adhesive, high and low temperature resistance, 1-2 mmthickness, 10 minutes or so, the initial curing, 5-6 hours basiccuring, a certain degree of strength. It takes at least 24 hours tocure. Single component, no need to mix, extrude and then smear onthe rest, * heating. 6. Kd -5606: UV curing adhesive, adhesivetransparent PS sheet and plate, can achieve no trace effect, needto use UV lamp irradiation curing. The effect is beautiful aftergluing. But the high temperature resistance ispoor.
优点:
1、具高强度及弹性系数、高冲击强度、使用温度范围广;
2、高度透明性及自由染色性;
3、H.D.T.高;
4、耐疲劳性佳;
5、耐候性佳;
6、电气特性优;
7、无味无臭对人体无害符合卫生安全;
8、成形收缩率低、尺寸安定性良好。
PC加工参数:
加工(熔体)温度:282-304度
模具温度:71.1-93.3度
背压:0.345到0.689 MPa
螺杆转速:40到70 rpm
排气孔深度:0.025到0.076 mm
干燥温度:121 度
干燥时间:3.0-4.0 hr
螺筒后部温度:260-282度
螺筒中部温度:271-293度
Advantages:1. High strength and elastic coefficient, high impact strength,wide application temperature range; 2. High transparency and freedyeing; 3. D. T. High; 4, good fatigue resistance; 5, good weatherresistance; 6, excellent electrical characteristics; 7, odorlessand harmless to health safety; 8, forming shrinkage rate is low,good size stability. PC processing parameters: processing (melt)temperature: 282-304 degrees die temperature: 71.1-93.3 degreesback pressure: 0.345 to 0.689 MPa screw speed: 40 to 70 rpm ventdepth: 0.025 to 0.076 mm dry temperature: 121 degrees dry time:3.0-4.0 hr screw rear temperature: 260-282 degrees screw middletemperature: 271-293 degrees
Vorteil:
1. Es hat hohe Festigkeit, elastischen Koeffizient, hoheSchlagfestigkeit und breite Palette der Nutzungstemperatur;
2. Hohe Transparenz und freie Färbung;
3.H.D.T. hoch;
4. Gute Ermüdungsbeständigkeit;
5. gute Witterungsbeständigkeit;
6. Ausgezeichnete elektrische Eigenschaften;
7. Geruchs- und geruchlos, harmlos für den menschlichen Körper,im Einklang mit Gesundheit und Sicherheit;
8. Geringe Formschrumpfung und gute Dimensionsstabilität.
PC-Verarbeitungsparameter:
Verarbeitung (Schmelze) Temperatur: 282-304 ℃
Formtemperatur: 71.1-93.3 Grad
Gegendruck: 0.345 bis 0.689 MPa
Schraubendrehzahl: 40 bis 70 rpm
Auspufflochtiefe: 0,025 bis 0,076 mm
Trocknungstemperatur: 121 ℃
Trocknungszeit: 3.0-4.0 hr
Temperatur an der Rückseite des Schraubenlaufs: 260-282 Grad
Temperatur in der Mitte des Schraubenfasss: 271-293 ℃
PC-Kunststoffverklebung
Folgende Klebstoffe können je nach Bedarf ausgewählt werden:
1.G-933: Einkomponentiger Normaltemperaturhärtender weicherelastischer stoßfester Klebstoff, beständig gegen hohe und niedrigeTemperaturen, mit unterschiedlicher Viskosität undKlebegeschwindigkeit von Sekunden bis Stunden.
2. KD-833 Sofortkleber kann verwendet werden, um PC-Plastik fürmehrere Sekunden oder Dutzende von Sekunden zu verbinden *.aber dieKlebeschicht ist hart und spröde und kann nicht in heißem Wasserüber 60 ℃ eingeweicht werden.
3. QN-505, Zweikomponentenkleber, weiche Klebeschicht, geeignetfür großflächige Verklebung oder Verbund von PC-Kunststoff.Allerdings ist die hohe Temperaturbeständigkeit schlecht.
4. QN-906: Zweikomponentenkleber, hohe Temperatur beständig.
5.G-988: Ein-Komponenten-Raumtemperatur vulkanisierter Gummi,nach dem Aushärten, ist das Elastomer mit gutem wasserdichten undstoßfesten Klebstoff, hohe und niedrige Temperaturbeständigkeit,1-2mm dick, etwa 10-Minuten der anfänglichen Aushärtung, 5-6Stunden der grundlegenden Aushärtung, mit einer bestimmten Stärke.Die Heilung dauert mindestens 24-Stunden. Einkomponentig, keinMischen, Auftragen und Aufstehen nach der Extrusion, *Aufheizen.
6. KD-5606: UV-UV-härtender Klebstoff wird verwendet, umtransparente PS-Blätter und Platten zu verbinden, um einenspurenfreien Effekt zu erzielen. Er muss durch ultravioletteLichtstrahlung ausgehärtet werden. Der Effekt ist schön nach demKleben. Allerdings ist die hohe Temperaturbeständigkeitschlecht.