DuPont Performance Polymers Delrin® 111P NC010 AcetalHomopolymer物性表
物理性能额定值 (公制)额定值 (英制)测试方法
| 比重 | 1.42 g/cc | 1.42 g/cc | ASTM D792 |
| 密度 | 1.42 g/cc | 0.0513 lb/in³ | ISO 1183 |
| Water Absorption | 0.30 % @Temperature 23.0°C | 0.30 % @Temperature 73.4°F | Immersion 24h; ASTM D570 |
| 1.0 % @Temperature 23.0°C | 1.0 % @Temperature 73.4°F | Saturation, immersed; ISO 62, Similar to | |
| 线性成型收缩率 | 0.017 - 0.020 cm/cm @Thickness 3.20mm | 0.017 - 0.020 in/in @Thickness 0.126in | Transverse, 24h; ASTM D955 |
| 0.018 - 0.021 cm/cm @Thickness 3.20mm | 0.018 - 0.021 in/in @Thickness 0.126in | Flow, 24h; ASTM D955 | |
| 线性模具收缩，Flow | 0.018 - 0.021 cm/cm @Thickness 4.00mm | 0.018 - 0.021 in/in @Thickness 0.157in | Parallel, 24h; ISO 294-4 |
| 0.021 cm/cm @Thickness 2.00mm | 0.021 in/in @Thickness 0.0787in | ISO 294-4 | |
| 线性成型收缩率,横向 | 0.019 cm/cm @Thickness 2.00mm | 0.019 in/in @Thickness 0.0787in | ISO 294-4 |
| 0.018 - 0.021 cm/cm @Thickness 4.00mm | Normal, 24h; ISO 294-4 | ||
| 熔体流动速率 | 1.0 g/10 min @Load 1.05 kg,Temperature 190 °C | 1.0 g/10 min @Load 2.31 lb,Temperature 374 °F | ASTM D1238 |
| 2.4 g/10 min @Load 2.16 kg,Temperature 190 °C | 2.4 g/10 min @Load 4.76 lb,Temperature 374 °F | ISO 1133 | |
| 化合物熔体指数 | 1.9 g/10 min @Load 2.16 kg,Temperature 190 °C | 1.9 g/10 min @Load 4.76 lb,Temperature 374 °F | cm3/10 min; ISO 1133 |
机械性能额定值 (公制)额定值 (英制)测试方法
| 洛氏硬度（M 级） | 92 | 92 | ISO 2039/2 |
| 洛氏硬度（R 级） | 120 | 120 | ISO 2039/2 |
| 121 | 121 | ASTM D785 | |
| 抗张强度 | 72.0 MPa @Temperature 23.0°C | 10400 psi @Temperature 73.4°F | 5mm/min (0.2in/min); ASTM D638 |
| 60.799 MPa @Strain 2.8574 %,Temperature -40.0 °C | 8818.2 psi @Strain 2.8574 %,Temperature -40.0 °F | ISO 527 | |
| 87.176 MPa @Strain 5.7149 %,Temperature -40.0 °C | 12644 psi @Strain 5.7149 %,Temperature -40.0 °F | ISO 527 | |
| 94.877 MPa @Strain 8.5723 %,Temperature -40.0 °C | 13761 psi @Strain 8.5723 %,Temperature -40.0 °F | ISO 527 | |
| 96.84 MPa @Strain 11.43 %,Temperature -40.0 °C | 14050 psi @Strain 11.43 %,Temperature -40.0 °F | ISO 527 | |
| 97.432 MPa @Strain 14.287 %,Temperature -40.0 °C | 14131 psi @Strain 14.287 %,Temperature -40.0 °F | ISO 527 | |
| 97.672 MPa @Strain 17.145 %,Temperature -40.0 °C | 14166 psi @Strain 17.145 %,Temperature -40.0 °F | ISO 527 | |
| 98.055 MPa @Strain 20.002 %,Temperature -40.0 °C | 14222 psi @Strain 20.002 %,Temperature -40.0 °F | ISO 527 | |
| 98.733 MPa @Strain 22.86 %,Temperature -40.0 °C | 14320 psi @Strain 22.86 %,Temperature -40.0 °F | ISO 527 | |
| 99.053 MPa @Strain 25.717 %,Temperature -40.0 °C | 14366 psi @Strain 25.717 %,Temperature -40.0 °F | ISO 527 | |
| 99.549 MPa @Strain 28.574 %,Temperature -40.0 °C | 14438 psi @Strain 28.574 %,Temperature -40.0 °F | ISO 527 |