抗张强度(屈服) | 72.0 MPa @Temperature 23.0°C | 5mm/min (0.2in/min); ASTM D638 | |
72.0 MPa @Temperature 23.0°C | ISO 527 | ||
伸长率 (断裂) | 40 % @Temperature 23.0°C | 40 % @Temperature 73.4°F | nominal; ISO 527 |
50 % @Temperature 23.0°C | 50 % @Temperature 73.4°F | ISO 527 | |
73 % @Temperature 23.0°C | 73 % @Temperature 73.4°F | 5mm/min (0.2in/min); ASTM D638 | |
Elongation at Yield | 20 % @Temperature 23.0°C | 20 % @Temperature 73.4°F | ISO 527 |
21 % @Temperature 23.0°C | 21 % @Temperature 73.4°F | 5mm/min (0.2in/min); ASTM D638 | |
拉伸模量 | 3.00 GPa @Temperature 23.0°C | 435 ksi @Temperature 73.4°F | 5mm/min (0.2in/min); ASTM D638 |
3.20 GPa @Temperature 23.0°C | 464 ksi @Temperature 73.4°F | ISO 527 | |
弯曲强度 | 80.0 MPa @Strain 3.50 %,Temperature 23.0 °C | 11600 psi @Strain 3.50 %,Temperature 73.4 °F | ISO 178 |
92.0 MPa @Strain 5.00 %,Temperature 23.0 °C | 13300 psi @Strain 5.00 %,Temperature 73.4 °F | ASTM D790 | |
弯曲模量 | 2.90 GPa @Temperature 23.0°C | 421 ksi @Temperature 73.4°F | ISO 178 |
2.97 GPa @Temperature 23.0°C | 431 ksi @Temperature 73.4°F | ASTM D790 | |
悬壁梁缺口冲击强度 | 0.960 J/cm @Temperature 23.0°C | 1.80 ft-lb/in @Temperature 73.4°F | ASTM D256 |
悬壁梁无缺口冲击强度 | NB @Temperature 23.0°C | NB @Temperature 73.4°F | ASTM D4812 |
悬壁梁缺口冲击强度 | 11.0 kJ/m² @Temperature -40.0°C | 5.23 ft-lb/in² @Temperature -40.0°F | ISO 180/1A |
11.0 kJ/m² @Temperature 23.0°C | 5.23 ft-lb/in² @Temperature 73.4°F | ISO 180/1A | |
简支梁无缺口冲击强度 | 27.0 J/cm² @Temperature -30.0°C | 128 ft-lb/in² @Temperature -22.0°F | ISO 179/1eU |
30.0 J/cm² @Temperature 23.0°C | 143 ft-lb/in² @Temperature 73.4°F | ISO 179/1eU | |
简支梁缺口冲击强度 | 0.900 J/cm² @Temperature -30.0°C | 4.28 ft-lb/in² @Temperature -22.0°F | ISO 179/1eA |
1.10 J/cm² @Temperature 23.0°C | ISO 179/1eA | ||
拉伸蠕变模量(1 hr) | 3000 MPa @Temperature 23.0°C | 435000 psi @Temperature 73.4°F | ISO 899 |
拉伸蠕变模量(1000 hr) | 1700 MPa @Temperature 23.0°C | 247000 psi @Temperature 73.4°F | ISO 899 |
电气性能额定值 (公制)额定值 (英制)测试方法
体积电阻率 | 8.00e+14 ohm-cm @Temperature 23.0°C | 8.00e+14 ohm-cm @Temperature 73.4°F | ASTM D257 |
表面电阻 | 6.00e+14 ohm @Temperature 23.0°C | 6.00e+14 ohm @Temperature 73.4°F | ASTM D257 |
介电常数 | 3.7 @Frequency 1.00e+6Hz, Temperature 23.0 °C | 3.7 @Frequency 1.00e+6Hz, Temperature 73.4 °F | ASTM D150 |
介电强度 | 18.0 kV/mm @Thickness 3.20 mm,Temperature 23.0 °C | 457 kV/in @Thickness 0.126 in,Temperature 73.4 °F | Short Time; ASTM D149 |
耗散因数 | 0.0050 @Frequency 1.00e+6Hz, Temperature 23.0 °C | 0.0050 @Frequency 1.00e+6Hz, Temperature 73.4 °F | ASTM D150 |
相比耐漏电起痕指数(CTI) | 600 V @Temperature 23.0°C | 600 V @Temperature 73.4°F | IEC 60112 |
600 V @Thickness 3.00 mm,Temperature 23.0 °C | 600 V @Thickness 0.118 in,Temperature 73.4 °F | UL 746A |
热性能额定值 (公制)额定值 (英制)测试方法
线形热膨胀系数 - 流动 | 500 µm/m-°C @Temperature 23.0 -55.0 °C | 278 µin/in-°F @Temperature 73.4 -131 °F | ASTM E 831 |
500 µm/m-°C @Temperature -40.0 -23.0 °C | 278 µin/in-°F @Temperature -40.0 -73.4 °F | ISO 11359-1/-2 | |
500 µm/m-°C @Temperature 23.0 -55.0 °C | ISO 11359-1/-2 | ||
500 µm/m-°C @Temperature 55.0 -100 °C | 278 µin/in-°F @Temperature 131 -212 °F | ISO 11359-1/-2 | |
线性热膨胀系数,横向流动 | 94.0 µm/m-°C @Temperature -40.0 -23.0 °C | 52.2 µin/in-°F @Temperature -40.0 -73.4 °F | ISO 11359-1/-2 |
110 µm/m-°C @Temperature 23.0 -55.0 °C | 61.1 µin/in-°F @Temperature 73.4 -131 °F | ASTM E 831 | |
110 µm/m-°C @Temperature 23.0 -55.0 °C | ISO 11359-1/-2 |