特性：
1.物理性能：摩擦系数低；硬度低，性差；粘附性差；具有生理惰性，； 2.力学性能：机械性能较差，易出现蠕变现象，具有冷流性；耐疲劳性好；拉伸、弯曲、冲击强度低；一般不用作结构件；3.耐热性能：使用温度-60℃-260℃； 4.燃烧性能：极限氧指数>95%，自熄性，是不燃物质； 5.化学稳定性：的化学稳定性、性；几乎对所有的化学试剂和溶剂是惰性的；6.电性能：优良的高频绝缘材料，的介电材料；7.耐候性能：耐候性、耐大气老化性好； 8.加工性：可采用注塑、挤出、模压加工；但临界剪切速率低，注塑挤出时出料速率和压力要低；
物理性能
Teflon® PFATE9724
Perfluoroalkoxy
DuPont Fluoropolymers
产品说明：
For inventory control purposes product name may be followed byan X.
Products labeled PFA TE9724 and PFA TE9724 X are e and allinformation in this document is applicable to both.
Typical Application
DuPont™ Teflon ® PFA TE9724 is an ideal resin for applicationsinvolving compounding and compression molding, as well as extrudedtubing and other profiles for hose, electrical insulators, andsleeving; industrial film and products made from film; andinjection or compression molded articles re superiorelectrical, chemical, and thermal properties. Teflon ® PFA TE9724offers a slightly higher melt flow rate than Teflon ® PFA TE9725,providing greater processing ease.
Description
DuPont™ Teflon ® PFA TE9724 is a general-purpose fluoroplasticresin available as loosely compacted fluff. It is intended for usein special application processes in consultation with DuPont.Compared with other grades of Teflon ® PFA, its most uni are a relatively high flow rate and properties that makeit suitable for a variety of processes and demanding end uses,especially compounding and compression molding. Table 1 shows thetypical property data for Teflon ® PFA TE9724.
Teflon ® PFA TE9724 is used when traditional extrusion and moldingprocesses are required for producing products with the superiorproperties of a fluoroplastic resin. Compared to otherthermoplastics, the high melt strength and thermal stability ofTeflon ® PFA TE9724 can be used to improve processing rates.Compared with other thermoplastics, Teflon ® PFA TE9724 provides asuperior balance and level of end-use properties at high servicetemperatures. Teflon ® PFA TE9724 combines the processing ease ofconventional thermoplastics with many properties similar to thoseof polytetrafluoroethylene.
Properly processed products made from neat Teflon ® PFA TE9724resin provide the superior properties characteristic offluoroplastic resins: chemical inertness, exceptional dielectricproperties, heat resistance, toughness and flexibility, lowcoefficient of friction, non-stick characteristics, negligiblemoisture absorption, low flammability, performance at temperatureextremes and excellent weather resistance.
In a flame situation, products of Teflon ® PFA TE9724 resistignition and do not promote flame spread. When ignited by flamefrom other sources, their contribution of heat is very small andadded at a slow rate with very little smoke.
Teflon ® PFA TE9724 meets the re of ASTM D3307, TypeI
物性信息：
| 基本信息 | |
|---|---|
| 特性 |
|
| 用途 |
|
| 形式 |
|
| 加工方法 |
|
| 物理性能 | 额定值 | 单位制 | 测试方法 |
|---|---|---|---|
| 比重 | 2.14 | g/cm³ | ASTM D792 |
| 熔流率（熔体流动速率） (372°C/5.0 kg) | 12 | g/10 min | ASTM D3307, ISO 12086 |
| 吸水率 (24 hr) | < 0.030 | % | ASTM D570 |
| 硬度 | 额定值 | 单位制 | 测试方法 |
|---|---|---|---|
| 肖氏硬度 (邵氏 D) | 55 | ASTM D2240, ISO 868 |
| 机械性能 | 额定值 | 单位制 | 测试方法 |
|---|---|---|---|
| 抗张强度 (23°C) | 25.0 | MPa | ASTM D3307, ISO 12086 |
| 伸长率 (断裂, 23°C) | 300 | % | ASTM D3307, ISO 12086 |
| 弯曲模量 (23°C) | 590 | MPa | ASTM D790, ISO 178 |
| 热性能 | 额定值 | 单位制 | 测试方法 |
|---|---|---|---|
| 熔融温度 | 305 | °C | ASTM D4591 |
| 电气性能 | 额定值 | 单位制 | 测试方法 |
|---|---|---|---|
| 体积电阻率 | 1.0E+18 | ohms·cm | ASTM D257, ISO 1325 |
| 介电强度 | |||
| 0.250mm 1 | 80 | kV/mm | ASTM D149 |
| 0.250 mm | 80 | kV/mm | IEC 60243-1 |
| 介电常数 (1 MHz) | 2.03 | ASTM D150, IEC 60250 | |
| 耗散因数 (1 MHz) | < 2.0E-4 | ASTM D150, IEC 60250 |
| 可燃性 | 额定值 | 单位制 | 测试方法 |
|---|---|---|---|
| UL 阻燃等级 2 | V-0 | UL 94 | |
| 极限氧指数 | > 95 | % | ASTM D2863, ISO 4589-2 |
| 补充信息 | 额定值 | 单位制 | 测试方法 |
|---|---|---|---|
| MIT Folding Endurance 3(200.0µm) | 1.5E+4 | Cycles | ASTM D2176 |
| Weather and Chemical Resistance: Outstanding |
1、为少量全氟丙基全氟乙烯基醚与聚四氟乙烯的共聚物。熔融粘结性增强，溶体粘度下降，而性能与聚四氟乙烯相比无变化。此种树脂可以直接采用普通热塑性成型方法加工成制品。
2、长期使用温度-196--260摄氏度，有 的耐化学腐蚀性，对所有化学品都 ，摩擦系数在塑料中，还有很好的电性能，其电绝缘性不受温度影响，有“塑料王”之称。
3、其耐化学药品性与聚四氟乙烯相似，比偏氟乙烯好。
4、其抗蠕变性和压缩强度均比聚四氟乙烯好，拉伸强度高，伸长率可达100-300%。介电性好，耐辐射性能阻燃性达V0级。
5、适于制作 件，减磨 件、密封件、绝缘件和医疗器械零件。
6、高温电线、电缆绝缘层，防腐设备、密封材料、泵阀衬套，和化学容器。
成型性能
1.结晶料,吸湿小。可采用通常得热塑性塑料得加工方法加工成制品。
2.流动性差，极易分解，分解时产生腐蚀气体。宜严格控制成型温度不要超过475摄氏度，模具应加热至150-200摄氏度，浇注系统对料流阻力应小。
3.半透明粒料，注塑、挤出成型。成型温度350-400摄氏度，475摄氏度以上容易引起变色或发生气泡。并注意脱模会较困难。
4、因熔融的材料对金属有腐蚀作用，长期生产，模具需要电镀铬处理。
全氟烷氧基树脂
PFA树脂相对来说是比较新的可熔融加工的氟塑料。
PFA的熔点大约为580F，密度为2.13— 2.16g/cc（克/立方厘米）。PFA与PTFE和FEP相似，但在302T以上时，机械性能略优于FEP，且可在高达500F下的温度下使用，它的耐化学品性与PTFE相当。PFA的产品形式有用于模塑和挤塑的粒状产品，用于旋转模塑和涂料的粉状产品；