PEI 基础创新塑料(美国) ATX200-1100 高强度, 耐化学性良好,燃料系统

机筒选择和螺杆设计注意事项：

加工PEI*树脂时，通常可以采用适用天相容螺杆和机筒的传统制造材料。建议使用双金属机筒。

根据螺杆直径，好使长径比为20:1，压缩比为2.2:1。还建议使用短进料区（5段）和长压缩区（11段），通过一个恒定的锥度逐渐过渡到一个较短的计量区（4段）。压缩应在一个逐渐过渡的恒定锥度上完成，因为急剧的变化可能导致过大的剪切力和材料降解。如果无法选择特定的螺杆，经证明使用长径比为16:1到24:1、压缩率为1.5:1到3.0:1的通用螺杆是成功的。建议不要使用带排气孔的机筒来加工PEI*树脂。止回阀应为滑动逆止环类型。在螺杆计量区中，通常流通间隙至少要占流动区域横断面的80%.

PEI无定形,具有杰出的耐高温、高强度、高模量及广泛的耐化学剂性，天性耐燃,且烟气排放量低，高的介电常数和损耗因数

Precautions for barrel selection and screw design:

When processing PEI * resin, traditional manufacturing materialssuitable for compatible screw and barrel can usually be used.Bi-metal barrel is recommended.

According to the screw diameter, the length-diameter ratio is20:1 and the compression ratio is 2.2:1. In addition, it is alsorecommended to use a short feed area (5 sections) and a longcompression area (11 sections), while gradually transitioning to ashorter metering area (4 sections) through a constant taper.Compression should be completed at a constant taper of gradualtransition, because sharp changes may lead to excessive shear forceand material degradation. If it is impossible to select a specificscrew, it has been proved that it is successful to use a universalscrew with a length-diameter ratio of 16:1 to 24:1 and acompression ratio of 1.5:1 to 3.0:1. It is not recommended to usethe barrel with exhaust hole to process PEI * resin. Check valvesshall be of the slip check ring type. In the screw metering area,the flow gap usually accounts for at least 80% of the cross sectionof the flow area

PEI amorphous, with excellent high temperature resistance, highstrength, high modulus and extensive chemical resistance, naturalflame resistance, low flue gas emission, high dielectric constantand loss factor

Vorsichtsmaßnahmen bei der Auswahl des Zylinders und derSchraubenkonstruktion:

Bei der Verarbeitung von PEI-Harz können üblicherweisetraditionelle Fertigungsmaterialien verwendet werden, die fürkompatible Schrauben und Zylinder geeignet sind. Bimetall-Lauf wirdempfohlen.

Entsprechend dem Schraubendurchmesser ist dasLänge-Durchmesser-Verhältnis 20:1 und das Kompressionsverhältnisist 2.2:1. Darüber hinaus wird empfohlen, einen kurzenZufuhrbereich (5-Abschnitte) und einen langen