聚甲醛为白色粉末，一般不透明，着色性好，比重1.41-1.43克/立方厘米，成型收缩率1.2-3.0%，成型温度170-200℃，干燥条件80-90℃2小时。POM的长期耐热性能不高，但短期可达到160℃，其中均聚POM短期耐热比共聚POM高10℃以上，但长期耐热共聚POM反而比均聚POM高10℃左右。可在-40℃~100℃温度范围内长期使用。POM极易分解，分解温度为280℃，分解时有刺激性和腐蚀性气体发生。故模具钢材宜选用耐腐蚀性的材料制作。

Polyformaldehyde is a white powder, generally opaque, with goodcoloring properties. Its specific gravity is 1.41-1.43 grams percubic centimeter, and its molding shrinkage is 1.2-3.0%. Themolding temperature is 170-200 ℃, and the drying condition is 80-90℃ for 2 hours. The long-term heat resistance of POM is not high,but it can reach 160 ℃ in the short term. Among them, theshort-term heat resistance of homopolymer POM is more than 10 ℃higher than that of copolymer POM, but the long-term heatresistance of copolymer POM is actually about 10 ℃ higher than thatof homopolymer POM. It can be used for a long time within thetemperature range of -40 ℃ to 100 ℃. POM is highly prone todecomposition, with a decomposition temperature of 280 ℃. Duringdecomposition, irritating and corrosive gases may occur. Therefore,the mold steel should be made of corrosion-resistantmaterials. Полиформальдегид для белого порошка, как правило,непрозрачный, хорошая окраска, удельный вес 1,41 - 1,43 г / см3,скорость усадки формования 1,2 - 3,0%, температура формования 170 -200 °C, условия сушки 80 - 90 °C 2 часа.  Долгосрочнаятеплостойкость POM невелика, но в краткосрочной перспективе можетдостигать 160 ° C, из которых краткосрочная теплостойкость POMвыше, чем у POM, но долгосрочная теплостойкость POM выше, чем у POMпримерно на 10 ° C.  Может использоваться в течениедлительного времени при температуре от - 40°C до 100°C.  POMочень легко разлагается, температура разложения составляет 280°C,при разложении происходит раздражающий и коррозионный газ. Поэтому пресс - форма сталь должна быть изготовлена из коррозионно- стойких материалов.