30%玻纤PA66美国杜邦 FR52G30BL

成核添加剂。用于制得微结晶尼龙,可加快脱模时间,使成型周期缩短20%~30%。根据用途不同,还可加增塑剂和润滑剂等。另一种改性的方法是共聚,共聚尼龙是良好的包覆材料和衬垫密封材料;聚酰胺与聚烯烃嵌段接枝共聚,可大幅度提高冲击强度和尺寸稳定性,降低吸湿性,甚至可制成易加工、低成本的塑料制品。这种解决聚酰胺缺陷的有效途径,是近年来发展改性品种的方向之一。

Nucleating additives. Used to produce microcrystalline nylon, itcan accelerate the demolding time and shorten the molding cycle by20% to 30%. In addition, plasticizers and lubricants can also beadded according to different purposes. Another modification methodis copolymerization, where copolymerized nylon is a good coatingmaterial and gasket sealing material; Polyamide and polyolefinblock grafting copolymerization can significantly improve impactstrength and dimensional stability, reduce moisture absorption, andeven make easily processed and low-cost plastic products. Thiseffective way to solve polyamide defects is one of the directionsfor developing modified varieties in recentyears.Nukleierungszusätze. Verwendet, um mikrokristallines Nylon zuproduzieren, kann es die Entformungszeit beschleunigen und denFormzyklus um 20% zu 30%. Darüber hinaus können Weichmacher undSchmierstoffe für unterschiedliche Zwecke hinzugefügt werden. Eineandere Modifikationsmethode ist die Copolymerisierung, bei dercopolymerisiertes Nylon ein gutes Beschichtungsmaterial undDichtungsmaterial ist; Die Copolymerisierung von Polyamid- undPolyolefinblocktransplantaten kann die Schlagfestigkeit undDimensionsstabilität erheblich verbessern, dieFeuchtigkeitsaufnahme reduzieren und sogar leicht verarbeitete undkostengünstige Kunststoffprodukte herstellen. Diese effektiveLösung von Polyamidfehlen ist eine der Richtungen für dieEntwicklung modifizierter Sorten in den letzten Jahren.