Polymist®F284
Polytetrafluoroethylene
Solvay Specialty Polymers
产品说明：
Polymist® F284 is a white micronized PTFE powder composed ofdiscrete particles.
Available worldwide, Polymist® F284 is a medium molecular weightgrade with excellent thermal stability, designed for use incritical high temperature engineering and high perfomancepolymers.
As with all Polymist® micronized powders, F284 offers excellentchemical and temperature resitence, low surface energy, lowcoeffcient of friction and good dispersion ability.
Main features of Polymist® F284 are:
Better wear resistance
Increased pressure x velocity (PV) limits
Reduced friction
Improved stick-slip response
Improved mold release
物性信息：
| 基本信息 | |
|---|---|
| 用途 |
|
| 外观 |
|
| 形式 |
|
| 物理性能 | 额定值 | 单位制 | 测试方法 |
|---|---|---|---|
| 比表面积 | 3.0 | m²/g | 内部方法 |
| 平均颗粒尺寸 - D50 | 9.0 | µm | 内部方法 |
| 体积密度 | 400 | g/l | ASTM D4895 |
| 补充信息 | 额定值 | 单位制 | 测试方法 |
|---|---|---|---|
| 含油研磨 | 5.00 | NPIRI | |
| 熔体温度 | 325 到 335 | °C | ASTM D3418 |
基本特点
耐高温——使用工作温度达250℃。
耐低温——具有良好的机械韧性；即使温度下降到-196℃，也可保持5%的伸长率。
耐腐蚀——对大多数化学药品和溶剂，表现出惰性、能耐强酸强碱、水和各种有机溶剂。
耐气候——有塑料中的老化寿命。
高润滑——是固体材料中摩擦系数di者。
不粘附——是固体材料中小的表面张力，不粘附任何物质。
无毒害——具有生理惰性，作为人工血管和脏器长期植入体内无不良反应。
聚四氟乙烯相对分子质量较大，低的为数十万，高的达一千万以上聚四氟乙烯，一般为数百万（聚合度在104数量级，而聚乙烯仅在103）。一般结晶度为90～95%，熔融温度为327～342℃。聚四氟乙烯分子中CF2单元按锯齿形状排列，由于氟原子半径较氢稍大，所以相邻的CF2单元不能完全按反式交叉取向，而是形成一个螺旋状的扭曲链，氟原子几乎覆盖了整个高分子链的表面。这种分子结构解释了聚四氟乙烯的各种性能。温度低于19℃时，形成13/6螺旋；在19℃发生相变，分子稍微解开，形成15/7螺旋。
虽然在全氟碳化合物中碳-碳键和碳-氟键的断裂需要分别吸收能量346.94和484.88kJ/mol，但聚四氟乙烯解聚生成1mol四氟乙烯仅需能量171.38kJ。所以在高温裂解时，聚四氟乙烯主要解聚为四氟乙烯。聚四氟乙烯在260、370和420℃时的失重速率（%）每小时分别为1×10-4．4×10-3和9×10-2。可见，聚四氟乙烯可在260℃长期使用。由于高温裂解时还产生剧毒的副产物氟光qi和全氟异ding烯等，所以要特别注意安全防护并防止聚四氟乙烯接触明火。