PVDF聚偏氟乙烯 美国苏威PVDF 20810-20 耐 磨性 铁氟龙材料
PVDF（聚偏氟乙烯) 在氟塑料中具有强韧性、低摩擦系数、耐老化性、耐气候，耐辐照性能好等特点。
特性：
1、可射出及押出之氟化树脂（俗称热可塑性铁氟龙）。
2、耐化学特性。
3、高机械强度及韧度。
4、耐候，抗紫外线及核射线。
5、耐热性佳并有高介电强度。
用途：耐化学性之零件、电线电缆等。
SolvaySpecialty Polymers Solef® 20810 PVDF Copolymer
Polyvinylidinefluoride (PVDF), Molded/Extruded
Solvay Specialty Polymers
产品说明：
Keyfeatures of this grade: Li Battery, Virgin. Recommended processingis solution. Available as powder & granules.
General information about SOLEF® PVDF: SOLEF®PVDF is a fluorinated semi-crystalline thermoplastic which isobtained by polymerizing vinylidene fluoride. Important propertiesinclude excellent chemical resistance to most aggressive substancesand solvents, excellent mechanical strength and toughness, highabrasion resistance, high temperature capabilities, excellent agingresistance, high purity, resistance to UV and nuclear radiation,excellent intrinsic fire resistance, resistance to weathering, lowpermeability to most gases and liquids, and easily melt-processedby standard methods of molding and extrusion.
Tensile properties are achieved with varying methods of samplefabrication. Information provided by Solvay Solexis, Inc.
物性信息：
| 物理性能 | 额定值 (公制) | 额定值 (英制) | 测试方法 |
|---|---|---|---|
| 密度 | 1.78 g/cc | 0.0643 lb/in³ | ISO 1183 |
| 吸水率 | <= 0.040 % | <= 0.040 % | ISO 62 (method 1) |
| 线性成型收缩率 | 0.020 - 0.030 cm/cm | 0.020 - 0.030 in/in | |
| 熔体流动速率 | 2.0 g/10 min @Load 2.16 kg, Temperature 230 °C | 2.0 g/10 min @Load 4.76 lb, Temperature 446 °F | ASTM D1238 |
| 6.0 g/10 min @Load 5.00 kg, Temperature 230 °C | 6.0 g/10 min @Load 11.0 lb, Temperature 446 °F | ASTM D1238 |
| 机械性能 | 额定值 (公制) | 额定值 (英制) | 测试方法 |
|---|---|---|---|
| 肖氏硬度 (邵氏 D) | 60 @Thickness 2.00 mm | 60 @Thickness 0.0787 in | ASTM D2240 |
| 极限抗拉强度 | 30.0 - 50.0 MPa | 4350 - 7250 psi | 50 mm/min; ASTM D638 |
| 抗张强度(屈服) | 15.0 - 18.0 MPa | 2180 - 2610 psi | 50 mm/min; ASTM D638 |
| 伸长率 (断裂) | 600 - 750 % | 600 - 750 % | 50 mm/min; ASTM D638 |
| 屈服伸长率 | 12 - 15 % | 12 - 15 % | 50 mm/min; ASTM D638 |
| 弹性模量 | 0.360 - 0.480 GPa | 52.2 - 69.6 ksi | 1 mm/min; ASTM D638 |
| 弯曲模量 | 0.360 - 0.440 GPa | 52.2 - 63.8 ksi | 2 mm/min; ASTM D790 |
| 悬壁梁缺口冲击强度 | 1.80 J/cm @Thickness 4.00 mm, Temperature 23.0 °C | 3.37 ft-lb/in @Thickness 0.157 in, Temperature 73.4 °F | Notched V 10 mm; ASTM D256 |
| 摩擦系数 | 0.20 - 0.30 | 0.20 - 0.30 | ASTM D1894 |
| 静态摩擦系数 | 0.20 - 0.40 | 0.20 - 0.40 | ASTM D1894 |
| 泰伯磨损，毫克/1000次 | 5.0 - 15 | 5.0 - 15 | CS10 / 1 kg |
| 电气性能 | 额定值 (公制) | 额定值 (英制) | 测试方法 |
|---|---|---|---|
| 电阻率 | >= 1.00e+14 ohm-cm | >= 1.00e+14 ohm-cm | Intensity = 10 mA after 2 min @ 23°C; ASTM D 257; DIN 53483 |
| 表面电阻 | >= 1.00e+14 ohm | >= 1.00e+14 ohm | Voltage < 1 V after 2 min - 500 V; ASTM D 257/DIN 53483 |
| 热性能 | 额定值 (公制) | 额定值 (英制) | 测试方法 |
|---|---|---|---|
| Heat of Fusion | 23.0 J/g | 9.89 BTU/lb | 80°C to end of melting |
| 24.0 J/g | 10.3 BTU/lb | Crystallization Heat | |
| 线性热膨胀系数 | 150 - 180 µm/m-°C @Temperature 20.0 °C | 83.3 - 100 µin/in-°F @Temperature 68.0 °F | ASTM D696 |
| 比热容 | 1.20 J/g-°C | 0.287 BTU/lb-°F | |
| 1.60 J/g-°C @Temperature 100 °C | 0.382 BTU/lb-°F @Temperature 212 °F | ||
| 导热系数 | 0.180 W/m-K | 1.25 BTU-in/hr-ft²-°F | ASTM C177 |
| 熔融温度 | 135 °C | 275 °F | Crystallinity by DSC; ASTM D 3418 |
| Crystallization Temperature | 92.0 °C | 198 °F | |
| 载荷下热变形温度(0.46 MPa) | 62.0 °C @Thickness 4.00 mm | 144 °F @Thickness 0.157 in | after annealing 150°C 16 hr; ASTM D648 |
| 载荷下热变形温度(1.8 MPa) | 40.0 °C @Thickness 4.00 mm | 104 °F @Thickness 0.157 in | after annealing 150°C 16 hr; ASTM D648 |
| 维卡软化温度 | 120 °C @Load 1.00 kg, Thickness 4.00 mm | 248 °F @Load 2.20 lb, Thickness 0.157 in | ISO 306 |
| 脆化温度 | -22.0 °C | -7.60 °F | ASTM D746A |
| 玻璃化转变温度，Tg | -29.0 °C | -20.2 °F | DMTA |
| 分解温度 | 330 - 350 °C | 626 - 662 °F | Thermal Stability via TGA : beginning - and at 1% weight loss inair |
| 极限氧指数 | 44 % @Thickness 3.00 mm | 44 % @Thickness 0.118 in | sheet; ASTM D2863 |
由于具有弹性、低重量、低导热性、高耐化学腐蚀性以及耐热性等多重优良性质，PVDF常用于制作电线的绝缘外皮。常用于绕线电路的细30号线以及印刷电路板常用PVDF绝缘。具有PVDF绝缘层的线缆常以PVDF的商标名而被称为“Kynar线”。
PVDF由于具有压电特性常用于生产触觉传感器阵列、廉价的应变仪以及轻量的音频换能器。
PVDF还是锂电池复合电极的标准粘结剂：将溶于N-甲基-2-吡咯烷酮（NMP）比重为1－2%的PVDF与石墨、硅、锡、LiCoO2、LiMn2O4或是LiFePO4这样的活性锂存储材料以及碳黑或碳纳米纤维这样的导电添加剂混合，然后将该浆料浇注在金属集电器并蒸发掉NMP即可形成复合电极或糊电极。PVDF之所以可以用于这个场合是因为其在电池充放电的电势范围内具有化学惰性并且不会与电解质或锂反应。
在生物医学领域，PVDF薄膜常用于***印迹，蛋白质会在上面电泳。由于PVDF耐溶剂腐蚀，因此检测中使用的薄膜可以轻易剥离并重复使用，以检测其他蛋白质。PVDF薄膜还可以用于制作注射器式或轮式的膜过滤装置。这种材料所具有的耐热、耐化学腐蚀以及低蛋白质结合等特性令其可以在制备***过程中用作消毒过滤器，并且在HPLC等分析的样品制备过程中还可作为过滤器，防止昂贵的设备因这些样品中少量的颗粒物质而损坏。
PVDF还可用于制作***单丝钓鱼线，以替代传统的尼龙单丝。其表面坚硬，更耐锋利的鱼齿磨损，并且其光密度比尼龙低，令鱼线更不易被敏锐的鱼眼发现。同时其密度比尼龙大，使鱼线可以更快地向着鱼下沉。